SEMI-CRYSTALLINE POLYMER TUBE, ADDITION POLYMERIZATION THROUGH ZIEGLER-NATTA CATALYSTS OR METALLOCENIC CATALYSTS WHICH MAKE A SYNTHESIS POSSIBLE AT LOW PRESSURES AND TEMPERATURES OBTAINING A POLYMER WITH A LOW DEGREE OF CHAIN BRANKING.
THIS POLYETHYLENE HAS THE HIGHEST DENSITY, BETWEEN 0.945 AND 0.970 g/cm 3 , CONSEQUENT TO THE HIGH CRYSTALLINITY AROUND 70% (PE LD IS AROUND 40%). LINEAR CHAINS RESULT IN A COMPACT PACKAGING WHICH DETERMINES HIGHER RESISTANCE, GOOD RESILIENCE, A LOW COEFFICIENT OF FRICTION, GOOD RESISTANCE TO WEAR AND A GREATER RANGE OF USE AND USE TEMPERATURES.
USE: PNEUMATIC OR HYDRAULIC USE IN HIGH DENSITY POLYETHYLENE
INDICATIVE RATIO BETWEEN AMBIENT TEMPERATURE AND NOMINAL PRESSURE PIPE DIAMETER T 20° - PN 100% T 30° - PN 80% T 40° - PN 70% T 50° - PN 60% T 60° - PN 50% T 70° - PN 45%
Colors: BLACK - NEUTRAL/WHITE on request Standard rolls 100 meters - 25 - 50 meters on request